Brand gas cylinders
are made of quality
manganese steel
or alloy steel through
solid drawn process
with advanced workmanship
and sophisticated
facilities to turn
the steel billets
into cylinders,
thus giving smooth
and bright surface,
homogeneous wall
thickness and precise
dimensions.
The steel cylinders
are manufactured
according to Chinese
National Standard
and inspected by
China Boiler and
High Pressure Container
Supervisor which
is an independent
superintendent organization.
Avaliable for export
are seamless steel
gas cylinders with
valves and caps
for industrial gases:
Oxygen, Argon, Hydrogen,
Nitrogen, Helium,
Freon, Carbon Dioxide,
Liquefied Ammonia,
and Oxygen for medical
use, Welded Liquefied
petroleum Gas Cylinders
and Chlorine Cylinders
etc.
Customers are always
welcome to place
orders with our
corporation. Catalogues
andinformation are
available upon request.
|
| |
|
|
|
| Type |
Outside
diameter |
Water
capacity |
Gas
capacity |
Wall
thickness |
Filling
gas |
Pressure |
Height |
Weight |
| Working |
Hydraulic |
|
| Y219-40/150 |
219mm |
40-42Lit |
6M3 |
5.8mm
Min. |
Oxygen |
150 |
250 |
1380 |
58¡À2 |
| Y219-45/150 |
219mm |
45-47Lit |
7M3 |
5.8mm
Min. |
Nitrogen
Air, |
150 |
250 |
1580 |
62¡À2 |
| Y232-40/150 |
232mm |
40-42Lit |
6M3 |
6.1mm
Min. |
Argon,
Helium, |
150 |
250 |
1375 |
58¡À2 |
| Y232-45/150 |
232mm |
45-47Lit |
7M3 |
6.1mm
Min. |
Hydrogen
Carbon
Dioxide. |
150 |
250 |
1430 |
65¡À2 |
|
|
| ¡¡¡¡Chemical
composition (%) |
| Material |
C |
Mn |
Si |
V |
Cr |
Mo |
S |
P |
|
| Mn-steel |
0.30-0.37 |
1.40-1.80 |
0.17-0.37 |
0.07-0.12 |
|
|
¡Ü0.040 |
¡Ü0.040 |
| Cr-Mo-Steel |
0.26-0.34 |
0.40-0.70 |
0.20-0.40 |
|
0.80-1.10 |
0.15-0.25 |
¡Ü0.040 |
¡Ü0.040 |
|
|
|
| ¡¡¡¡Mechanical
property: |
| Material |
Yield
strength (N/mm2) |
Tensile
Strength |
Elongation
(%) |
Impact
value |
Flatting |
|
| Mn-steel |
¡Ý529 |
¡Ý735 |
¡Ý16 |
¡Ý49(U-notch)
(-20oC) |
8S |
| Cr-Mo-Steel |
¡Ý675 |
¡Ý795 |
¡Ý14 |
¡Ý
49(U-notch)
(-50oC) |
no-crack |
|
|
 Meaning
of stamp mark in drawing
as foloow:
1.Mark of manufacture
2.Serial Number
3.Hydraulic test pressure
(kg/cm2)
4.Working pressure (kg/cm2)
5.Actual weight (kg)
6.Actual water capacity
(Lit)
7.Design wall thickness
for cylinder portion
8.Inspection mark of manufacturer
and production date
9.Supervision and inspection
mark
10.Mark of gas cylinder
used in cold region |
|
|
| |
| Type |
Iutside
diameter |
Nominal
volume
|
Actual
volume
|
Wall
thick-ness |
Length
mm |
Weight |
Fusible
Plug |
| Body |
Total |
Amount |
Melting
point |
|
| Dg350-80 |
350mm |
80Lit |
80Lit |
6mm |
990 |
1135 |
58.5kg |
|
|
| Dg350-100 |
350mm |
100Lit |
100Lit |
6mm |
1185 |
1330 |
69.3kg |
| Dg350-125 |
350mm |
125Lit |
125Lit |
6mm |
1485 |
1630 |
85kg |
| Dg600-400 |
600mm |
400Lit |
420Lit |
8mm |
1586 |
1850 |
260kg |
3 |
70¡À5oC£c |
| Dg600-400 |
600mm |
400Lit |
420Lit |
10mm |
1586 |
1850 |
365kg |
3 |
| Dg800-800 |
800mm |
800Lit |
840Lit |
10mm |
1750 |
2150 |
466kg |
6 |
| Dg800-800 |
800mm |
800Lit |
840Lit |
12mm |
1750 |
2150 |
660kg |
6 |
|
|
|
| Filling
gas |
Working
pressure |
Test
pressure |
Temperature
in use |
Filling
ratio kg/l |
| Hydraulic |
Air |
|
| Chlorine
(Cl2)
|
20kg/cm2 |
30kg/cm2 |
20kg/cm2 |
-40¡«60oC |
1.25 |
| Difluor-dichloro
methane (F12) |
1.14 |
| Ammonia
(NH3) |
30kg/cm2 |
45kg/cm2 |
30kg/cm2 |
0.53 |
| difluor-chloro
methane (f22) |
1.02 |
|
|