| Stainless Steel Electrode |
|
|
|
| Elec-trode
Name |
Equiva-lent
Specifi-cation |
Type
of Coating |
Welding
Posi-tion |
Elec-trode
Diameter mm(inch) |
Current
& Pola-rity |
Mechanical
Properties of Weld Metal |
| Tensite
Strength (MPa) |
Elongation |
| SH.
A002 |
AWS E308L-16
JIS D308L-16
GB E00 19-10-16 |
Lime-Titania |
F,V,OH,H |
2.0(5/64)
2.5(3/32)
3.2(1/8)
4.0(5/32)
5.0(13/64) |
AC
or DC |
¡Ý520 |
¡Ý35 |
| |
| SH.A022 |
AWS E316L-16
JIS D316L-16
GB E00-18-12Mo2-16 |
Lime-Titania |
F,V,OH,H |
2.0(5/64)
2.5(3/32)
3.2(1/8)
4.0(5/32)
5.0(13/64) |
AC
or DC |
¡Ý490 |
¡Ý30 |
| |
| SH.
A102 |
AWS E308-16
JIS D308-16
GB E0-19-10-16 |
Lime-Titania
|
F,V,OH,H |
2.0(5/64)
2.5(3/32)
3.2(1/8)
4.0(5/32)
5.0(13/64) |
AC
or DC |
¡Ý550 |
¡Ý35 |
| |
| SH.
A132 |
AWS E347-16
JIS D347-16
GB E0-19-10 Nb-16 |
Lime-Titania |
F,V,OH,H |
2.0(5/64)
2.5(3/32)
3.2(1/8)
4.0(5/32)
5.0(13/64) |
AC
or DC |
¡Ý520 |
¡Ý25 |
| |
| SH.
A202 |
AWS E316-16
JIS D316-16
GB E0-18-12No2-16 |
Lime-Titania |
F,V,OH,H |
2.0(5/64)
2.5(3/32)
3.2(1/8)
4.0(5/32)
5.0(13/64) |
AC
or DC |
¡Ý520 |
¡Ý30 |
| |
| SH.
A212 |
AWS E316Nb-16
GB E0-18-12Mo,2Nb-16 |
Lime-Titania
|
F,V,OH,H |
2.0(5/64)
2.5(3/32)
3.2(1/8)
4.0(5/32)
5.0(13/64) |
AC
or DC |
¡Ý550 |
¡Ý25 |
| |
| SH.
A222 |
AWS E316Cu-16
GB E0-19-13Mo2Cu-16 |
Lime-Titania |
F,V,OH,H |
2.0(5/64)
2.5(3/32)
3.2(1/8)
4.0(5/32)
5.0(13/64) |
AC
or DC |
¡Ý540 |
¡Ý25 |
| |
| SH.
A242 |
AWS E317-16
GB
E0-19-13Mo3-16 |
Lime-Titania |
F,V,OH,H |
2.0(5/64)
2.5(3/32)
3.2(1/8)
4.0(5/32)
5.0(13/64) |
AC
or DC |
¡Ý550 |
¡Ý25 |
| |
| SH.
A302 |
AWS E309-16
JIS D309-16
GB E1-23-13-16 |
Lime-Titania
|
F,V,OH,H |
2.0(5/64)
2.5(3/32)
3.2(1/8)
4.0(5/32)
5.0(13/64) |
AC
or DC |
¡Ý550 |
¡Ý25 |
| |
| SH.
A312 |
AWS E309Mo-16
JIS D309-Mo-16
GB E1-23-13Mo2-16 |
Lime-Titania |
F,V,OH,H |
2.0(5/64)
2.5(3/32)
3.2(1/8)
4.0(5/32)
5.0(13/64) |
AC
or DC |
¡Ý550 |
¡Ý25 |
| |
| SH.
A402 |
AWS E310-16
GB E2-26-21-16 |
Lime-Titania |
F,V,OH,H |
2.0(5/64)
2.5(3/32)
3.2(1/8)
4.0(5/32)
5.0(13/64) |
AC
or DC |
¡Ý550 |
¡Ý25 |
| |
| SH.
A412 |
AWS E310Mo-16
GB E1-26-21Mo2-16 |
Lime-Titania
|
F,V,OH,H |
2.0(5/64)
2.5(3/32)
3.2(1/8)
4.0(5/32)
5.0(13/64) |
AC
or DC |
¡Ý550 |
¡Ý25 |
| |
|
|
| Electrode
Name |
Chemical
Composition of Weld Metal (%) |
| C |
Mn |
Si |
Cr |
Ni |
other
elements |
| SH.
A002 |
¡Ü0.04 |
0.5~2.5 |
¡Ü0.90 |
18.0~21.0 |
9.0~11.0 |
- |
| Characteristics
and Applications:A lime-titania coating
AC/DC electrode for welding extra low
carbon stainless steel or structural
steel subjected to working temperatures
below 300oC and corrosion. |
| SH.A022 |
¡Ü0.04 |
0.5~2.5 |
¡Ü0.09 |
17.0~20.0 |
11.0~14.0 |
Mo2.0~2.5 |
| Characteristics
and Applications:A lime-titania coating
AC/DC electrode with an extra low carbon
content in weld metal.It is intended
for welding Cr stainless steel. |
| SH.
A102 |
¡Ü0.08 |
0.5~2.5 |
¡Ü0.90 |
18.0~21.0 |
9.0~11.0 |
- |
| Characteristics
and Applications:A low-carbon stainless
steel electrode with lime-titania coating,suitable
for welding for welding 0Cr19Ni9 or0Cr18Ni11Ti
stainless steel subjected to working
temperatures below 300oC
and corrosion |
| SH.
A132 |
¡Ü0.08 |
0.5~2.5 |
¡Ü0.90 |
18.0~21.0 |
9.0~11.0 |
Nb8xC~1.00 |
| Characteristics
and Applications:A lime-titania coating
AC/DC electrode with niobium as stabilizing
agent.It is suitable for welding titanium
stabilized 0Cr 18Ni11Ti stainless steel
subjected to corrosion |
| SH.
A202 |
¡Ü0.08 |
0.5~2.5 |
¡Ü0.90 |
17.0~20.0 |
11.0~14.0 |
Mo2.0~2.5 |
| Characteristics
and Applications:A low carbon stainless
steel electrode with lime-titania coating.AC/DC
current. Suitable for welding 0Cr18Ni12Mo2
stainless steel or structures subjected
to acid.Also suitable for welding thin
plates. |
| SH.
A212 |
¡Ü0.08 |
0.5~2.5 |
¡Ü0.90 |
17.0~20.0 |
11.0~14.0 |
M02.0~2.5
Nb8xC~1.00 |
| Characteristics
and Applications:A lime-titania coating
electrode with niobium as stabilizing
agent.It is suitable for welding 0Cr
18Ni12Mo2, 00Cr17Ni14M02 stainless steel
or structures subjected to corrosion.AC/DCcurrent.Especially
good for welding thin plates. |
| SH.
A222 |
¡Ü0.08 |
0.5~2.5 |
¡Ü0.90 |
18.0~21.0 |
12.0~14.0 |
Cu~2
Mo 2.0~2.5 |
| Characteristics
and Applications:A lime-titania coating
electrode for welding stainless steel
with copper content,especially for welding
structures subjected to acid or corrosion
,such as H2SO4 |
| SH.
A242 |
¡Ü0.08 |
0.5~2.5 |
¡Ü0.90 |
18.0~21.0 |
12.0~14.0 |
Mo3.0~4.0 |
| Characteristics
and Applications:A lime-titania coating
electrode for welding stainless steel,with
higher content of Mo in weld metal.It
is intended for welding structures subjected
to pit corrosion. |
| SH.
A302 |
¡Ü0.15 |
0.5~2.5 |
¡Ü0.90 |
22.0~25.0 |
12.0~14.0 |
- |
| Characteristics
and Applications:A lime-titania coating
electrode for welding stainless steel,high-Cr
steel and high-Mn steel.Suitable for
joining of 308 stainless steel to mild
steel. |
| SH.
A312 |
¡Ü0.12 |
0.5~2.5 |
¡Ü0.90 |
22.0~25.0 |
12.0~14.0 |
Mo2.0~3.0 |
| Characteristics
and Applications:A lime-titania coating
electrode for welding stainless steel,higher
ability of corrosion resistance due
to the Mo content in weld metal.AC/DC
current.It is intended for welding structures
subjected to acid,such as H2SO4 |
| SH.
A402 |
¡Ü0.20 |
1.0~2.5 |
¡Ü0.75 |
25.0~28.0 |
20.0~22.5 |
- |
| Characteristics
and Applications:A lime-titania coating
Cr26Ni21 stainless steel electrode for
welding structures subjected to high
temperature of 900oC~1000oC,AC/DC
current |
| SH.
A412 |
¡Ü0.12 |
1.0~2.5 |
¡Ü0.075 |
2.50~28.0 |
20.0~22.5 |
Mo2.0~3.0 |
| Characteristics
and Applications:A lime-titania coating
Cr26Ni2Mo2 stainless steel electrode
for welding structures subject to high
temperature. |
|
|
| Non-Ferrous Material Welding
Wire and Electrode (Tin Brass Welding Rod) |
|
|
|
| Electrode
Name |
Equivalent
Specification |
Type
of Alloy |
Electrode
Diameter mm(inch) |
|
| SW.221 |
GB
HSCuZn-2 |
Copper
Base Alloys |
2.0(5/64)
5.0(13/64) 3.0(1/8) 6.0(15/64) 4.0(5/32) |
| SH.S222 |
AWS
RBCuZn-C |
Copper
Base Alloys |
2.0(5/64)
5.0(13/64) 3.0(1/8) 6.0(15/64) 4.0(5/32) |
| SH.Cu227 |
AWS
ECuSn-C |
Copper
Base Alloys |
3.2(1/8)
4.0(5/32) 5.0(13/64) |
|
|
| Electrode
Name |
Typical
Chemical Composition Weld Metal (%) |
| Sn |
Si |
Mn |
Fe |
C |
other
elements |
| SW.221 |
0.8~1.2 |
0.15~0.35 |
- |
- |
- |
Cu59~61
Zn bal. |
| Characterisitics
and Application: A high quality tin
brass gas welding rod that fuses readily
at 890oC.Recommended for
welding brass and braze-welding copper,bronze,steel
and cast iron. |
| SH.S222 |
0.7~1.0 |
0.05~0.15 |
0.03~0.1 |
0.35~1.2 |
- |
Cu
57~59 Zn bal. |
| Characterisitics
and Application: Low Fuming Bronze is
designed as a strong, hard brass welding
rod. For modern high-speed production
requirements for general repair.Fusing
temperature is 880oC |
| SH.Cu227 |
7.0~9.0 |
- |
- |
- |
bal |
P0.05~0.3 |
| Characterisitics
and Application: The phosphor bronze
electrode has exceptional control and
ease of manipulation. Recommended for
joining copper,copper-zinc,dissimilar
metals and as an over lay on cast iron
or steel.DC(reverse polarity) |
|
|
|
|
|
|
|